Integrated ESD protection method and system

ABSTRACT

An ESD structure is created on an integrated circuit by providing a conductive polymer material between a signal line and a supply node or ground reference. The conductive polymer material becomes conductive when an electric field of sufficient intensity is applied. In one embodiment, the concentration of conductive particles of the conductive polymer material is empirically determined so that the resulting film becomes conducting at a predetermined threshold voltage. The conductive polymer is applied in liquid form on the wafer surface using a silk-screen printing process or a spin-on process and then cured. The conductive polymer layer can be adapted for use in multilevel metallization systems.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to protection in an integrated circuit against electrostatic discharge (ESD). In particular, the present invention relates to integrating conductive polymer material on-chip to provide ESD protection.

2. Discussion of the Related Art

Mixing conductive and semi-conductive particles in an insulating polymer matrix can create a conductive polymer. In one instance, the conductive particles are aluminum spheres of several hundredths of a micron in diameter and each coated in a ceramic film several angstroms thick. Using an appropriate concentration of these conductive particles in the insulating polymer matrix, the particles can be spaced sufficiently close to each other to allow Fowler-Nordheim tunneling to occur. An example of such a polymer material, called “Surgx”, can be obtained from Surgx Corporation, Fremont, Calif.

The conductive polymer described above is insulating below certain electric field intensity (e.g. 10 volts per micron), but becomes highly conductive when the electric field intensity threshold is reached. FIG. 1 shows an electrical characteristic of a conductive polymer film. As shown in FIG. 1, as voltage is increased from 0 volts to about 5 volts (segment 103) across the conductive polymer film, the conductive polymer film is substantially insulating until threshold or “trigger” point 100 is reached. At trigger point 100, the conductive polymer film exhibits a “snap-back” phenomenon, in which the conductivity of the polymer film increases rapidly. As shown in FIG. 1, during snap-back, the voltage across conductive polymer film drops rapidly along segment 102, and thereafter, the current through the conductive polymer film increases substantially along segment 101. If the electrical field across the conductive polymer film is subsequently returned to a voltage below the snap-back voltage, however, the conductive polymer film returns to the pre-trigger insulating condition.

SUMMARY OF THE INVENTION

The present invention provides a method for creating a conductive polymer material on a semiconductor wafer. The conductive polymer material can be used to provide electrostatic discharge (ESD) protection in an integrated circuit.

In one embodiment of the present invention, the conductive polymer can be formed by: (a) applying on the surface of a semiconductor wafer a liquid film including polyamic acid, an organic solvent, and conductive particles; and (b) curing the liquid film at a sufficiently high temperature to cause polymerization of the polyamic acid and to evaporate the organic solvent to form a conductive polymer layer. The conductive polymer layer can be patterned by first providing a patterned masking layer over the conductive polymer layer; and etching the conductive layer in the presence of the patterned masking layer.

In an ESD application, the surface of the semiconductor wafer is first provided a patterned metallization layer prior to applying the liquid film. To provide ESD protection in a multilevel metallization system, a second layer of patterned metallization can be provided over the conductive polymer layer. In one embodiment including multilevel metallization, a dielectric layer is deposited over a first patterned metallization layer; and then openings are provided in the dielectric layer to form vias connecting metal lines in the first metallization layer to a subsequently formed second metallization layer. In that configuration, the conductive polymer material fills the via openings in the dielectric layer.

The concentration of the conductive particle in the conductive polymer material can be empirically determined. A sufficient concentration of the conductive particles is provided so that the conductive polymer becomes conducting when an electric field having an intensity above a predetermined threshold is applied across the polymer material.

In one embodiment, a passivation layer is provided above the conductive polymer layer. In one embodiment, the curing step is carried out by: (a) baking the liquid film at a first temperature over a predetermined time interval to create a polymerized layer without substantial cross-linking; and (b) baking the polymerized layer at a second temperature lower than the first temperature over a second time interval sufficient to eliminate the organic solvent. In another embodiment, after the organic solvent is eliminated, a hard curing step is carried out by baking the polymerized layer at a third temperature above the second temperature. The third temperature is selected to be sufficiently high to allow a cross-linking reaction in the polymerized layer to complete. If the polymer film is to be patterned, the hard curing step can be carried out simultaneously as the hard baking step in conventional processing of a developed photoresist layer.

According to the present invention, an ESD structure includes: (a) a first metal line provided on a semiconductor substrate for carrying an electrical signal; (b) a second metal line provided on the semiconductor substrate for carrying a supply voltage or a ground reference; and (c) a conductive polymer material in contact with the first and second metal lines. When the conductive polymer material becomes conductive when a sufficiently high voltage appears across the first and the second metal lines, such as when an electrostatic charge appears on the first metal line, the electrostatic charge is shunted to the supply voltage node or the ground reference. In one configuration, the polymer material is patterned. In another configuration, the conductive polymer material is provided as a blanket layer. In a third configuration, the first and second metal lines being provided on two levels of metallization. In a fourth configuration, the conductive polymer material fills openings in an interconnect dielectric layer. In that configuration, the openings connect metal lines in different levels of a multilevel metallization system. An insulating passivation layer is typically provided over the entire structure for mechanical protection.

The present invention is better understood upon consideration of the detailed description below and the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows an electrical characteristic of a conductive polymer film.

FIG. 2a shows configuration 200 for protection against ESD in an integrated circuit, in accordance with the present invention.

FIG. 2b shows configuration 220 for protection against ESD in an integrated circuit, in accordance with the present invention.

FIG. 2c shows configuration 240 for protection against ESD in an integrated circuit, in accordance with the present invention.

FIG. 2d shows configuration 260 for protection against ESD in an integrated circuit, in accordance with the present invention.

In these figures, and in the detailed description below, like elements are provided like reference numerals.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

In one embodiment of the present invention, a liquid Surgx material is obtained which includes a polyamic acid, and conductive and non-conductive particles suspended in an n-methyl-propyrrolidene (NMP) solvent.

The liquid Surgx material is applied on the surface of a semiconductor wafer using either a spin-on process or a silkscreen printing process. In a spin-on process, the liquid Surgx material has preferably a viscosity of 5 to 15 Kcps. A film thickness of about 25 microns or less can easily be formed. The Surgx material is then allowed to partially polymerize at a temperature between 200° C. to 300° C. for two hours. Then, the solvent in the partially polymerized film is then substantially completely evaporated at a temperature between 100° C. to 120° C. for two hours. At this point, the partially polymerized film is said to be “soft-cured”.

Then, a layer of photoresist is applied on the surface of the soft-cured partially polymerized film, exposed and developed using conventional photolithographical techniques to provide a pattern in the photoresist layer. The semiconductor wafer, which now includes the soft-cured partially polymerized film and the developed photoresist layer is then subject to a conventional “hard bake” step to harden the developed photoresist layer at between 200° C. to 250° C. for two hours. During this step, the soft-cured partially polymerized film becomes “hard-cured”, i.e., cross-linking in the polymerized film takes place, to create a conductive polymer film having the electrical characteristics shown in FIG. 1. For a given application, the necessary breakdown characteristics (i.e., the threshold or trigger point) can be empirically determined by varying the concentration of non-conductive and conductive particles.

The pattern in the photoresist layer can then be transferred into the polymer film using a conventional etch process in a polyimide etcher (e.g., a polyimide etcher obtainable from Hitachi Corporation, Japan).

The conductive polymer film thus formed can be used to protect an integrated circuit against electrostatic discharge (ESD). One example of a structure for protection against ESD, in accordance with the present invention is provided by configuration 200 of FIG. 2a. In FIG. 2a, metal traces 202 a, 202 b and 202 c are fabricated on the surface of semiconductor substrate 201. A polymer film is then formed and patterned using the method described above to provide conductive polymer traces 203 a and 203 b. A passivation layer 204 (e.g., borophosphosilicon glass) is then provided over the surface of the wafer. In configuration 200, metal traces 202 a and 202 c are, for example, input leads for receiving external signals into the integrated circuits, and are thus exposed to electrostatic discharge from an external source. Metal trace 202 b can be a lead connected to either a supply voltage node or a ground reference. When an ESD event occurs, say at metal trace 202 a, the charge associated with the ESD event creates momentarily a voltage difference between metal trace 202 b and metal trace 202 a. Polymer trace 203 a limits this voltage difference to the trigger voltage (e.g., 5 to 10 volts) and becomes conductive. Consequently, the charge in metal trace 202 a is shunted through polymer trace 203 a to metal trace 202 b to the ground reference or the supply node, thus preventing a high voltage from being developed on metal trace 202 a. Damage in the electronic circuits coupled to metal trace 202 a is thereby avoided.

FIG. 2b shows another configuration 220 for protection against ESD in an integrated circuit, in accordance with the present invention. In configuration 220, a blanket conductive polymer layer 203 is provided. Since patterning is not required, the photoresist application, exposure, development and etching steps are not necessary. The soft-cured partially polymerized layer is instead hard-cured at a temperature between 200° C. to 250° C. for two hours to form conductive polymer layer 203. Passivation layer 204 is then provided on conductive polymer layer 203.

FIG. 2c shows third configuration 240 for protection against ESD in an integrated circuit, in accordance with the present invention. In FIG. 2c, configuration 240 includes two levels of interconnect metallization represented by metal traces 202 a, 202 b, 205 a and 205 b. Conductive polymer layer 203 is provided between the two levels of interconnect metallization. The metal layer forming metal traces 205 a and 205 b can be formed and processed in a conventional manner on the surface of conductive polymer layer 203.

FIG. 2d shows fourth configuration 260 for protection against ESD in an integrated circuit, in accordance with the present invention. As in FIG. 2c, two levels of metallization represented by metal traces 202 a, 202 b, 205 a and 205 b are provided. However, instead of a blanket polymer layer 203, interlayer dielectric layer 206 (e.g., a deposited oxide layer) is provided over metal traces 202 a and 202 b. Subsequently, via openings are created in interlayer dielectric layer and filled by conductive polymer material to form conductive polymer vias 207 a and 207 b.

The detailed description above is provided to illustrate the specific embodiments of the present invention and is not intended to be limiting. Numerous modifications and variations within the scope of the present invention are possible. The present invention is set forth in the following claims. 

We claim:
 1. A method for electrostatic discharge protection for a semiconductor device, comprising: selecting a ratio of conductive particles to nonconductive particles within a liquid film; applying said liquid film on the surface of a semiconductor wafer said liquid film including conductive and nonconductive particles in said selected ratio, polyamic acid, and an organic solvent; and curing said liquid film at a sufficiently high temperature to cause polymerization of said polyamic acid and to evaporate said organic solvent to form a polymer layer; wherein said polymer layer has a trigger voltage related to said ratio of conductive particles to nonconductive particles, such that said polymer layer becomes conductive when a voltage above said trigger voltage is applied across said polymer layer.
 2. A method as in claim 1, further comprising: providing a patterned masking layer over said polymer layer; and etching said polymer layer in the presence of said patterned masking layer.
 3. A method as in claim 1, wherein said surface of said semiconductor wafer is provided a patterned metallization layer prior to said applying step.
 4. A method as in claim 3, further comprising providing a second layer of patterned metallization over said polymer layer.
 5. A method as in claim 3, further comprising, prior to said applying step: depositing a dielectric layer over said patterned metallization layer; and providing in said dielectric layer openings for contacting said patterned metallization layer.
 6. A method as in claim 1, further comprising providing a passivation layer above said polymer layer.
 7. A method as in claim 1, wherein said curing comprises: baking said liquid film at a first temperature over a predetermined time interval to create a polymerized layer without substantial cross-linking; and baking said polymerized layer at a second temperature lower than said first temperature over a second time interval sufficient to eliminate said organic solvent.
 8. A method as in claim 7, said curing further comprises, subsequent to baking said polymerized layer at said second temperature, baking said polymerized layer at a third temperature above said second temperature to provide said conductive polymer layer, said third temperature being sufficiently high to allow cross-linking reaction in said polymerized layer.
 9. The method of claim 3, wherein said first patterned metallization layer comprises at least one input lead and at least one reference lead, wherein said at least one input lead is capable of receiving electrostatic discharge, and wherein said reference lead carries a selected voltage, further comprising: receiving electrostatic discharge on at least one said input lead, said electrostatic discharge having a voltage; when the difference between said voltage of said electrostatic discharge and said voltage of said reference lead exceeds said trigger voltage, conducting through said polymer layer at least a portion of said electrostatic discharge from said at least one input lead to said reference lead.
 10. The method of claim 9, wherein said reference lead is connected to ground.
 11. The method of claim 9, wherein said reference lead is a voltage supply node.
 12. The method of claim 9, wherein said input lead is adjacent to said reference lead.
 13. The method of claim 4, wherein said first patterned metallization layer comprises at least one reference lead and wherein said second patterned metallization layer comprises at least one input lead, wherein said at least one input lead is capable of receiving electrostatic discharge, and wherein said reference lead carries a selected voltage, further comprising: receiving electrostatic discharge on at least one said input lead, said electrostatic discharge having a voltage; when the difference between said voltage of said electrostatic discharge and said voltage of said reference lead exceeds said trigger voltage, conducting through said polymer layer at least a portion of said electrostatic discharge from said at least one input lead to said reference lead.
 14. The method of claim 13, wherein said reference lead is connected to ground.
 15. The method of claim 13, wherein said reference lead is a voltage supply node.
 16. The method of claim 4, wherein said first patterned metallization layer comprises at least one input lead and wherein said second patterned metallization layer comprises at least one reference lead, wherein said at least one input lead is capable of receiving electrostatic discharge, and wherein said reference lead carries a selected voltage, further comprising: receiving electrostatic discharge on at least one said input lead, said electrostatic discharge having a voltage; when the difference between said voltage of said electrostatic discharge and said voltage of said reference lead exceeds said trigger voltage, conducting through said polymer layer at least a portion of said electrostatic discharge from said at least one input lead to said reference lead.
 17. The method of claim 16, wherein said reference lead is connected to ground.
 18. The method of claim 16, wherein said reference lead is a voltage supply node.
 19. The method of claim 5, wherein one said lead of each said pair is an input lead and the other said lead of each said pair is a reference lead, wherein said at least one input lead is capable of receiving electrostatic discharge, and wherein said reference lead carries a selected voltage, further comprising: receiving electrostatic discharge on at least one said input lead, said electrostatic discharge having a voltage; when the difference between said voltage of said electrostatic discharge and said voltage of said reference lead exceeds said trigger voltage, conducting at least a portion of said electrostatic discharge across said leads of at least one said pair of said leads.
 20. The method of claim 19, wherein said reference lead is connected to ground.
 21. The method of claim 19, wherein said reference lead is a voltage supply node.
 22. A method as in claim 3, further comprising, prior to said applying step: depositing a dielectric layer over said patterned metallization layer; providing in said dielectric layer openings for contacting said patterned metallization layer, wherein said liquid film enters said openings and forms at least a portion of said polymer layer therein; and providing a second layer of patterned metallization over said polymer layer, wherein said first layer of patterned metallization and said second layer of patterned metallization each comprise a plurality of conductive leads, wherein at least one pair of leads is formed, each said pair comprising one said lead in said first layer and one corresponding said lead in said second layer, wherein each said pair of said leads is separated by said polymer layer formed within a single said opening. 